347是含鈮的奧氏體不銹鋼，347H是其高碳版本。從成分上看，347可看作是在304不銹鋼的基礎上加入鈮元素而成。鈮是一種稀土元素，其作用同鈦較為相似，加入合金后能細化晶粒、抵抗晶間腐蝕及促進時效硬化。
現貨：圓棒、板材、鍛件、特殊尺寸可訂貨！
標準對照
|
中國
|
GB/T 20878-2007
|
06Cr18Ni11Nb
(0Cr18Ni11Nb)
|
07Cr18Ni11Nb
(1Cr19Ni11Nb)
|
|
美國
|
ASTM A240-15a
|
S34700，347
|
S34709，347H
|
|
日本
|
JIS G 4304:2005
|
SUS 347
|
—
|
|
德國
|
EN 10088-1:2005
|
X6CrNiNb18-10
1.4550
|
X7CrNiNb18-10
1.4912
|
成分規范-347
|
牌號
|
06Cr18Ni11Nb
|
347
|
SUS 347
|
1.4550
|
|
C
|
≤0.08
|
≤0.08
|
≤0.08
|
≤0.08
|
|
Si
|
≤1.00
|
≤0.75
|
≤1.00
|
≤1.00
|
|
Mn
|
≤2.00
|
≤2.00
|
≤2.00
|
≤2.00
|
|
P
|
≤0.045
|
≤0.045
|
≤0.045
|
≤0.045
|
|
S
|
≤0.030
|
≤0.030
|
≤0.030
|
≤0.015
|
|
Ni
|
9.0~12.0
|
9.0~13.0
|
9.0~13.0
|
9.0~12.0
|
|
Cr
|
17.0~19.0
|
17.0~19.0
|
17.0~19.0
|
17.0~19.0
|
|
Nb
|
10C~1.10
|
10C~1.00
|
≥10×C%
|
10C~1.00
|
成分規范-347H
|
牌號
|
07Cr18Ni11Nb
|
347H
|
1.4912
|
|
C
|
0.04~0.10
|
0.04~0.10
|
0.04~0.10
|
|
Si
|
≤1.00
|
≤0.75
|
≤1.00
|
|
Mn
|
≤2.00
|
≤2.00
|
≤2.00
|
|
P
|
≤0.045
|
≤0.045
|
≤0.045
|
|
S
|
≤0.030
|
≤0.030
|
≤0.015
|
|
Ni
|
9.0~12.0
|
9.0~13.0
|
9.0~12.0
|
|
Cr
|
17.0~19.0
|
17.0~19.0
|
17.0~19.0
|
|
Nb
|
8C~1.10
|
8C~1.00
|
10C~1.20
|
物理性能
|
密度（g/cm3）20℃
|
8.03
|
|
熔點（℃）
|
1398~1427
|
|
比熱容 [kJ/(kg·K)] 0~100℃
|
0.50
|
|
熱導率 [W/(m·K)]
|
100℃
|
16.3
|
|
500℃
|
22.2
|
|
線膨脹系數（10-6/K）
|
0~100℃
|
16.6
|
|
0~500℃
|
18.6
|
|
電阻率（Ω·mm2/m）20℃
|
0.73
|
|
縱向彈性模量（kN/mm2）20℃
|
193
|
|
磁性
|
冷變形后稍有磁性
|
材料性能
①與304不銹鋼相當的優良耐蝕性。
②在427~816℃之間，能夠抑制碳化鉻形成，抗敏化，具有良好的耐晶間腐蝕性能。
③在816℃高溫的強氧化環境中，仍具有一定的抗蠕變強度。
④容易延展成形，容易焊接。
⑤良好的低溫韌性。
總體而言，347不銹鋼的性能相似于321（304加Ti）而更優于321；347H的碳含量更高，其抗蠕變強度及高溫強度相比347，得到進一步加強。
應用場合
347&347H不銹鋼高溫性能優于304及321，廣泛應用于航空，石油化工，食品，造紙等工業中，例如航空發動機的排氣總管和支管，渦輪壓氣機熱氣管道以及在小載荷及溫度不超過850℃條件下工作的零件等。
|